Abstract
Most attempts to synthesize graphynes are limited to using irreversible coupling reactions, which often result in the formation of nanometre-scale materials that lack long-range order. Here the periodically sp–sp2-hybridized carbon allotrope, γ-graphyne, was synthesized in bulk via a reversible dynamic alkyne metathesis of alkynyl-substituted benzene monomers. The balance between kinetic and thermodynamic control was managed through the simultaneous use of two different hexa-alkynyl-substituted benzenes as the comonomers to yield crystalline γ-graphyne. Additionally, the ABC staggered interlayer stacking of the graphyne was revealed using powder X-ray and electron diffraction. Finally, the folding behaviour of the few-layer graphyne was also observed on exfoliation, and showed step edges within a single graphyne flake with a height of 9 nm.
This is a preview of subscription content, access via your institution
Access options
Subscribe to this journal
Receive 12 digital issues and online access to articles
$119.00 per year
only $9.92 per issue
Buy this article
- Purchase on Springer Link
- Instant access to full article PDF
Prices may be subject to local taxes which are calculated during checkout
Similar content being viewed by others
Data availability
Experimental data and characterization data are provided in the Supplementary Information. Crystallographic data for the structure HPB reported in this Article has been deposited at the Cambridge Crystallographic Data Centre (CCDC), under deposition number 2111647. Copies of the data can be obtained free of charge via https://www.ccdc.cam.ac.uk/structures/.
Change history
14 July 2022
A Correction to this paper has been published: https://doi.org/10.1038/s44160-022-00136-y
References
Kroto, H. W., Heath, J. R., O’Brien, S. C., Curl, R. F. & Smalley, R. E. C60: buckminsterfullerene. Nature 318, 162–163 (1985).
Iijima, S. Helical microtubules of graphitic carbon. Nature 354, 56–58 (1991).
Novoselov, K. S. et al. Electric field effect in atomically thin carbon films. Science 306, 666–669 (2004).
Fan, Q. et al. Biphenylene network: a nonbenzenoid carbon allotrope. Science 372, 852–856 (2021).
Kaiser, K. et al. An sp-hybridized molecular carbon allotrope, cyclo[18]carbon. Science 365, 1299–1301 (2019).
Malko, D., Neiss, C., Viñes, F. & Görling, A. Competition for graphene: graphynes with direction-dependent Dirac cones. Phys. Rev. Lett. 108, 086804 (2012).
Chen, J., Xi, J., Wang, D. & Shuai, Z. Carrier mobility in graphyne should be even larger than that in graphene: a theoretical prediction. J. Phys. Chem. Lett. 4, 1443–1448 (2013).
Kang, J., Li, J., Wu, F., Li, S.-S. & Xia, J.-B. Elastic, Electronic, and Optical Properties of Two-Dimensional Graphyne Sheet. J. Phys. Chem. C 115, 20466–20470 (2011).
Peng, Q., Ji, W. & De, S. Mechanical properties of graphyne monolayers: a first-principles study. Phys. Chem. Chem. Phys. 14, 13385–13391 (2012).
Cranford, S. W. & Buehler, M. J. Mechanical properties of graphyne. Carbon 49, 4111–4121 (2011).
Zhang, Y. Y., Pei, Q. X. & Wang, C. M. Mechanical properties of graphynes under tension: s molecular dynamics study. Appl. Phys. Lett. 101, 081909 (2012).
Hirsch, A. The era of carbon allotropes. Nat. Mater. 9, 868–871 (2010).
Baughman, R. H., Eckhardt, H. & Kertesz, M. Structure–property predictions for new planar forms of carbon: layered phases containing sp2 and sp atoms. J. Chem. Phys. 87, 6687–6699 (1987).
Kehoe, J. M. et al. Carbon networks based on dehydrobenzoannulenes. 3. Synthesis of graphyne substructures. Org. Lett. 2, 969–972 (2000).
Johnson, C. A., Lu, Y. & Haley, M. M. Carbon networks based on benzocyclynes. 6. Synthesis of graphyne substructures via directed alkyne metathesis. Org. Lett. 9, 3725–3728 (2007).
Haley, M. M. Synthesis and properties of annulenic subunits of graphyne and graphdiyne nanoarchitectures. Pure Appl. Chem. 80, 519–532 (2008).
Kilde, M. D. et al. Synthesis of radiaannulene oligomers to model the elusive carbon allotrope 6,6,12-graphyne. Nat. Commun. 10, 3714 (2019).
Gao, Y. et al. The loss of endgroup effects in long pyridyl-endcapped oligoynes on the way to carbyne. Nat. Chem. 12, 1143–1149 (2020).
Eisler, S. & Tykwinski, R. R. Expanded radialenes: modular synthesis and characterization of cross-conjugated enyne macrocycles. Angew. Chem. Int. Ed. 38, 1940–1943 (1999).
Tahara, K. et al. Syntheses and properties of graphyne fragments: trigonally expanded dehydrobenzo[12]annulenes. Chem. Eur. J. 19, 11251–11260 (2013).
Tahara, K. et al. Control and induction of surface-confined homochiral porous molecular networks. Nat. Chem. 3, 714–719 (2011).
Tahara, K., Yoshimura, T., Ohno, M., Sonoda, M. & Tobe, Y. Syntheses and photophysical Properties of boomerang-shaped bis(dehydrobenzo[12]annulene) and trapezoid-shaped tris(dehydrobenzo[12]annulene). Chem. Lett. 36, 838–839 (2007).
Zhang, W., Brombosz, S. M., Mendoza, J. L. & Moore, J. S. A high-yield, one-step synthesis of o-phenylene ethynylene cyclic trimer via precipitation-driven alkyne metathesis. J. Org. Chem. 70, 10198–10201 (2005).
Diederich, F. & Kivala, M. All-carbon scaffolds by rational design. Adv. Mat. 22, 803–812 (2010).
Grave, C. & Schlüter, A. D. Shape-persistent, nano-sized macrocycles. Eur. J. Org. Chem. 2002, 3075–3098 (2002).
Zhang, W. & Moore, J. S. Shape-persistent macrocycles: structures and synthetic approaches from arylene and ethynylene building blocks. Angew. Chem. Int. Ed. 45, 4416–4439 (2006).
Li, G. et al. Architecture of graphdiyne nanoscale films. Chem. Commun. 46, 3256–3258 (2010).
Li, Y., Xu, L., Liu, H. & Li, Y. Graphdiyne and graphyne: from theoretical predictions to practical construction. Chem. Soc. Rev. 43, 2572–2586 (2014).
Huang, C. et al. Progress in research into 2D graphdiyne-based materials. Chem. Rev. 118, 7744–7803 (2018).
Pan, Q. et al. Direct synthesis of crystalline graphtetrayne—a new graphyne allotrope. CCS Chem. 3, 1368–1375 (2021).
Li, Q. et al. Synthesis of γ-graphyne by mechanochemistry and its electronic structure. Carbon 136, 248–254 (2018).
Li, Q., Yang, C., Wu, L., Wang, H. & Cui, X. Converting benzene into γ-graphyne and its enhanced electrochemical oxygen evolution performance. J. Mater. Chem. A 7, 5981–5990 (2019).
Ding, W., Sun, M., Zhang, Z., Lin, X. & Gao, B. Ultrasound-promoted synthesis of γ-graphyne for supercapacitor and photoelectrochemical applications. Ultrason. Sonochem. 61, 104850 (2020).
Diederich, F. Carbon scaffolding: building acetylenic all-carbon and carbon-rich compounds. Nature 369, 199–207 (1994).
Cao, Y. et al. Unconventional superconductivity in magic-angle graphene superlattices. Nature 556, 43–50 (2018).
Zhou, H., Xie, T., Taniguchi, T., Watanabe, K. & Young, A. F. Superconductivity in rhombohedral trilayer graphene. Nature 598, 434–438 (2021).
Fürstner, A. The ascent of alkyne metathesis to strategy-level status. J. Am. Chem. Soc. 143, 15538–15555 (2021).
Ma, T. et al. Single-crystal X-ray diffraction structures of covalent organic frameworks. Science 361, 48–52 (2018).
Hu, Y. et al. Single crystals of mechanically entwined helical covalent polymers. Nat. Chem. 13, 660–665 (2021).
Jin, Y. H., Yu, C., Denman, R. J. & Zhang, W. Recent advances in dynamic covalent chemistry. Chem. Soc. Rev. 42, 6634–6654 (2013).
Du, Y. et al. Highly active multidentate ligand-based alkyne metathesis catalysts. Chem. Eur. J. 22, 7959–7963 (2016).
Narita, N., Nagai, S., Suzuki, S. & Nakao, K. Optimized geometries and electronic structures of graphyne and its family. Phys. Rev. B 58, 11009–11014 (1998).
Zhou, J. et al. Electronic structures and bonding of graphyne sheet and its BN analog. J. Chem. Phys. 134, 174701 (2011).
Srinivasu, K. & Ghosh, S. K. Graphyne and graphdiyne: promising materials for nanoelectronics and energy storage applications. J. Phys. Chem. C 116, 5951–5956 (2012).
Scharber, M. C. & Sariciftci, N. S. Low band gap conjugated semiconducting polymers. Adv. Mater. Technol. 6, 2000857 (2021).
Acknowledgements
We thank J. Choi (University of Colorado Boulder) for helpful discussions on the electrochemistry tests and B. Lama (University of Colorado Boulder) for solid-state NMR spectroscopy data acquisition. W.Z. acknowledges the National Science Foundation (DMR-1420736). Y.Z. acknowledges the National Natural Science Foundation of China (31202117). Y.H. thanks the Summer Graduate Fellowship support from University of Colorado Boulder. The authors gratefully acknowledge use of the Materials Research X-Ray Diffraction Facility at the University of Colorado Boulder (RRID: SCR_019304), with instrumentation supported by NSF MRSEC grant DMR-1420736.
Author information
Authors and Affiliations
Contributions
Y.H., Y.Z. and W.Z. conceived the idea and led the project. Y.H., S.H., J.W. and L.J.W. conducted the synthesis. C.W. conducted the modelling. Q.P. and Y.Z. conducted the transmission electron microscopy. R.L. and M.B.R. conducted the AFM. V.M. and N.A.C. conducted the WAXS. Y.H., Y.J., Y.Z. and W.Z. interpreted the results and Y.H., Y.J. and W.Z. wrote the manuscript.
Corresponding authors
Ethics declarations
Competing interests
Y.H. and W.Z. are inventors on a US patent application submitted by University of Colorado Boulder. The other authors do not have any competing interests.
Peer review
Peer review information
Nature Synthesis thanks the anonymous reviewers for their contribution to the peer review of this work. Primary Handling editor: Peter Seavill, in collaboration with the Nature Synthesis team.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Supplementary Information
Experimental Details and Supplementary Figs. 1–28, discussion and Tables 1–4.
Supplementary Data 1
Crystallographic data of 1,2,3,4,5,6-hexapropynylbenzene (HPB), CCDC 2111647
Source data
Source Data Fig. 4c
The Excel sheet contains height plot data for the layered structure of exfoliated γ-graphyne.
Rights and permissions
About this article
Cite this article
Hu, Y., Wu, C., Pan, Q. et al. Synthesis of γ-graphyne using dynamic covalent chemistry. Nat. Synth 1, 449–454 (2022). https://doi.org/10.1038/s44160-022-00068-7
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1038/s44160-022-00068-7
This article is cited by
-
PHOTH-graphene: a new 2D carbon allotrope with low barriers for Li-ion mobility
Scientific Reports (2024)
-
Masked alkynes for synthesis of threaded carbon chains
Nature Chemistry (2024)
-
The first year of Nature Synthesis
Nature Synthesis (2023)
-
Porphene and porphite as porphyrin analogs of graphene and graphite
Nature Communications (2023)
-
On-surface synthesis of a doubly anti-aromatic carbon allotrope
Nature (2023)